TAC膜

VA液晶一枚式

VA液晶二枚式

IPS液晶

QWF 3D Glass

Properties.

Unit

Q9C5 GL 60mic

Dimensions

Thickness gage

Mic

61

Optical

Retardation Ro

Nm

125±10

Retardation Rth

nm

0.6

Haze

%

0.21

L*(Photometer)

nm

97.12

a*(Photometer)

nm

0.004

b*(Photometer)

nm

0.11

Transmission at 550nm

%

92.7

Physical

Heat shirinkage (90℃ / 24hr) MD/TD

%

-0.209

-0.117

Moisture expansion for Sumika standard (20℃ / 85%24hr) MD/TD

%

0.119

0.116

Water vapor transmission rate

g/m2-day

142.56

Mechanical

Tensile Strength, MD/TD

Kgf/mm2

10.48

10.43

Yeild Strength, MD/TD

Kgf/mm2

10.45

10.21

Elongation, MD/TD

%

4.23

7.90

E-Modulus, MD/TD

Kgf/mm2

386.65

362.85

PROPERTIES

UNIT

P900 GL

P905 GL

P915 GL

P908 GL

P916 GL

P940 GL

P960 GL

P980 GL

Thickness (mean)

µm

50±3

50±3

50±3

187±5

187±5

40±3

60±3

80±3

µm

80±3

80±3

80±3

Thickness TD　[max-min]

µm

≤6

≤6

≤6

≤12

≤12

----　　

----　　

----　　

Knurling, distance to edge

mm

1-2

1-2

1-2

----　

　----　

----　　

----　　

----　　

Friction µS

≤0.6

≤0.6

≤0.6

　----　

　----　

----　　

----　　

----　　

Haze

%

<1.0

<1.0

<1.0

<0.3

<0.4

<1.0

<1.0

<1.0

Transmission [380 nm]

%

<5

<1.0

----　　

1.8-3.7 (400nm)

----　　

0-6

0-6

0-6

Total transmission

%

≥92.0

≥92.0

≥92.0

≥91.5

≥91.5

≥92.0

≥92.0

≥92.0

Residual solvent

%

≤1.0

≤1.0

≤1.0

　----　

　----　

≤0.8

≤0.8

≤0.8

Product
Name
產品名稱

Substrate
Thickness
（μm）
基材厚度

Hardness
(H)
硬度

Adhesive
Thickness
（μm）
膠材厚度

Total Thickness
（μm）
材料總厚度

Total Light
Transmittance
（％）透光率

適用範圍

備註

THC086(TAC)

80um

2~3H

X

86±10%

92以上

For TFT, TN/STN

(UV, non-UV)

THC0J6(TAC)

190um

H~2H

X

196±10%

92以上

For SunGlass

(UV, non-UV)